road marking powder coating thermo plastic traffic paint

$500.00
1-24 Tons
$450.00
25-49 Tons
$430.00
>=50 Tons
Min. Order
1 Ton
GET LATEST PRICE ON APP
Choose your specifications
Company Information

Zhejiang Luyou Transportation Engineering New Materials Co., Ltd.

CN Manufacturer, Trading Company
Response Time
---
Response Rate:
---
Transactions
---
1 Year Paid Supplier Gold Supplier Onsite Check
Learn More

Quick Details

Port: Ningbo port;In Shanghai port
Payment Terms: L/C,T/T
Supply Ability: 200 Ton/Tons per Day
CAS No.: 64742-16-1
Other Names: road marking paint powder
MF: CCaO3
EINECS No.: 231-072-3
Place of Origin: Zhejiang China
Main Raw Material: Petroleum resin
Usage: Road Marking Paint
Application Method: Brush
State: Powder Coating
Brand Name: LUYOU
Model Number: Hot melt type
Product Name: Powder Coating
Model Number: Hot melt type
Colors: Golden yellow & white&
Main Raw Materials: Calcium carbonate, Glass beads, Resin, Titanium dioxide
Application: Hot-melt road marking paint
Softening Point: 90 ~ 120 ℃
Glass bead content: 18 ~ 25%
Construction temperature: 200℃ ± 20 ℃
Package: 25kg thermoplastic road marking paint per plastic woven bag
Advantage: Factory sales
Packaging Detail: Waterproof bag;25 KG/bag
Product Description

Testing standard:JT/T 280-2004《Road marking paint》

Detection unit:Academy of sciences, ministry of transport
The test items
Technical indicators
Test results
note




Coating appearance
fter drying, there should be no wrinkles, spots, bubbles, cracks, off, adhere to the tire phenomenon, the color and appearance of the coating and standard version is not much different.




Meet the requirements
The density of(g/m³)
1.80~2.30
2.1
Softening point(℃)
90~125
102
Non-stick tire drying time(min)

≤3

3
The compressive strength(Mpa)

≥12

28
Wear resistance(mg)
≤80
48

Resistance to water
No abnormality was found after 24 hours of water immersion

Meet the requirements



Alkali resistance
No abnormality was found after 24 hours soaking in saturated limestone water


Meet the requirements

fluidity(S)
35±10
42

Glass bead content(%)
18~25
25

The brightnefactorss 
≥0.75
0.85



Low temperature crack resistance of coating
Keep it at -10℃ for 4h, and leave it at room temperature for 4h for a cycle. After three consecutive cycles, there should be no cracks


Meet the requirements



Heating stability
Keep it at 200℃~220℃ for 4h under stirring condition, and there should be no obvious yellowing, coking, caking and other phenomena



Meet the requirements
Detailed Images
Packing & Delivery
;