|Port:||Tianjin Qingdao Shanghai|
|Supply Ability:||30000 Ton/Tons per Month Fire Clay Brick|
|Place of Origin:||China|
|MgO Content (%):||International Standard|
|Refractoriness (Degree):||Common (1580°< Refractoriness< 1770°)|
|SiC Content (%):||International Standard|
|Raw material:||clay,kaolin, Bauxite aggregate|
|Model Number:||Fire Clay Brick|
|Softening Temperature under load,0.2Mpa:||1350|
|CaO Content (%):||International Standard|
|Cold Crushing Strength:||≤25|
|Product name:||Fire Clay Brick|
|Al2O3 Content (%):||32|
|CrO Content (%):||International Standard|
|Apparent Porosity,% ≤:||20-24|
|SiO2 Content (%):||International Standard|
|Application:||Heat Furnace,Roller Kiln Roof|
|Packaging Detail:||Fire Clay Brick pacakge information: 1.Pallet+Paper or Steel angle bead+Paper board +Plastic or Steel belt +Plastic film 2.Can make the package according to customer's requirements.|
Furnace Pizza Stove Masonry Lining Standard Size Fire Clay Refractory Brick Price Per Tone
clay refractory bricks is a kind of refractory fire clay brick, the bauxite and flint clay as main raw material with add the sillimanite and the andalusite, the binder according to the proportion, then forming the low porosity clay products after mixing, molding, and drying.
Clay bricks of over SK30 contain over 30% Alumina and are made from raw materials of unusually high degree of purity of Bauxite and refractory clay. For serve under severe conditions,Rewell clay Alumina bricks have excellent mechanical strength, good resistance to thermal spalling, and are highly resistant to chemical attack by vilatile alkaies and some slag. We manufacture and design alumina bricks to meet the requirements of a great variety of service conditions thorough quality control.
Clay fire brick is one of the most common fire bricks. Its Al2O3 content is between 30% and 48%. The clay fired bricks are made of refractory clay or kaolin and clay clinker combined with clay, which is formed by semi-dry or plastic method and roasted at the temperature of 1250-1420.
Characteristics of clay refractory bricks:
1. Low porosity and strong density.
2. Good resistance to permeability and good corrosion resistance.
3. High temperature strength, long service life.
clay refractory bricks index
Softening Temperature under load,0.2Mpa
Apparent Porosity,% ≤
Cold crushing strength,Mpa ≥