Low Smoke Free of Halogen SILANE XLPE CrossLinking Polyolefin lszh Compound

$6.00 - $8.00
Min. Order
25 Kilograms
GET LATEST PRICE ON APP
Company Information

GO YEN CHEMICAL INDUSTRIAL CO., LTD.

TW Manufacturer
Response Time
>72h
Response Rate:
20%
Transactions
---
11 Years Paid Supplier Gold Supplier Onsite Check Trade Assurance
Learn More

Quick Details

Port: Kaohsiung
Payment Terms: L/C,T/T,Western Union
Supply Ability: 20000 Kilogram/Kilograms per Month
Place of Origin: Taiwan, China
Brand Name: GYC
Model Number: GY-SL-5001
Density: 1.45
Tensile Strength: 13 MPA
Elongation at Break: 175 %
HCI and HBr content: 0 mg/g
Delivery Detail: Within 7 Days
Packaging Detail: 25Kg/bag, Stored at cool place away from direct sunlight.
Product Description

LSFOH Polyolefin Compound


GY-SL-5001 belongs to silane cross-liking low smoke flame retardant polyolefin compound (lszh compound) without halogen. It is a combination of Halogen-free masterbatch and silane XLPE. GY-SL-5001 features excellent electrical performance, physical properties, stability and can be applied to low-voltage wire & cable insulation and sheathing. 

Properties
Item
Spec.
Value
Density
-
1.45
g/cm3
Tensile Strength
≧10
13
MPa
Elongation at Break
≧150
175
%
Heat elongation (200℃ x 15min x 0.2MPa)
Maximum elongation change under load
≦100
85
%
Maximum permanent elongation change after cooled
≦25
5
%
Volume resistance (20℃)
≧1 x 1012
1.5 x 1013
Ω.m
Volume resistance (90℃)
≧2 x 108
1.5 x 109
Ω.m
Oxygen index
≧30
32
%
HCI and HBr content
≦0.5
0
mg/g
HF content
≦0.1
0
mg/g
Suggested Methods

1. Extrusion for most PVC equipment. Processing technique is as following

*Ratio of length and diameter       18-25:1
*Screw diameter                              45-120 minutes
*Compressing Ratio                        1.5-2.5
*Filtering mesh                                 40/60/40


2. Processing Temperature

Feeding Zone
Compression Zone
Metering Zone
Neck
Die
110-120℃
120-130℃
130-140℃
140-150℃
140-150℃

3. Crosslinking
- Extruded cables can be fast crosslinked when bathed in 80-90℃ hot water.
- Low pressure steam bath at 80-90℃ can help crosslinking, too.
- Avoid overly high temperature to prevent from adhesion.
- The crosslinking time depends on the thickness of the insulation layer and size of coil.

Packing & Delivery

25 KG/Bag