Lower density polyarylamide compound/Engineering special plastic 30%CF reinforced PARA/Solvay PARA Ixef 3008

$15.30
Min. Order
25 Kilograms
Choose your specifications
Company Information

Jiangsu Seavay New Material Co., Ltd.

CN Trading Company
Response Time
<24h
Response Rate:
88.9%
Transactions
---
5 Years Paid Supplier Gold Supplier Onsite Check
Learn More

Quick Details

Place of Origin: United States
Brand Name: Solvay
Model Number: Ixef 3008
Color: Black
Fill&amp;Additive: Carbon Fiber
Material: PARA
Features: High Flow,High Stiffness,Good Strength,Outstanding Surface Finish
Uses: Industrial,Electrical/Electronic Applications,Automotive
RoHS Compliance: Contact Manufacturer
Forms: Pellets
Processing Method: Injection Molding
Delivery Detail: 2 days after payment
Selling Units: Single item
Single package size: 65X43X15 cm
Single gross weight: 25 KG
Package Type: 25kg/bag, 1ton/pallet

Aesthetics and Strength – A Beautiful Combination

Ixef® compounds typically contain 50-60% glass fiber reinforcement, giving them remarkable strength and rigidity. What makes them unique is that even with high glass loadings, the smooth, resin-rich surface delivers a high-gloss, glass-free finish that’s ideal for painting, metallization or producing a naturally reflective shell.

High Flow into Thin Walls

In addition, Ixef® PARA is an extremely high-flow resin so it can readily fill walls as thin as 0.5 mm, even with glass loadings as high as 60%.

Ixef® PARA Properties

Ixef® compounds are available in a variety of grades that are formulated to meet specific application requirements. A side-by-side comparison of typical properties provides a quick overview of performance capabilities.

Excellent Surface Finish

 

Superb, resin-rich surface provides a highly polished appearance, even with high glass fiber content.

Very High Strength and Stiffness 

 

The tensile and flexural strength of Ixef compounds are similar to many cast metals and alloys at ambient temperature. Ixef 1032 (60% glass fiber) exhibits typical values of 280 MPa and 400 MPa respectively at 23°C (73°F).

TENSILE PROPERTIES COMPARISON*
MaterialTensile Strength 
at Break, MPa
Tensile Modulus, 
GPa
Ixef 1022 (50% glass fiber)28020
Ixef 1032 (60% glass fiber)28024
Tin Bronze300105
Brass250105
Annealed Zinc150105
Zinc Alloy (4% Al, 0.04% Mg)28085
Annealed Aluminum (99.6%)7069
Duralumin19074
Al Ag3 Alloy14069

*ASTM Test Method at 23°C (73°F)

Very Low Creep

 

The creep resistance of Ixef compounds is superior to that of most engineering polymers with similar glass fiber content. Deformation of Ixef 1032 is less than 1% after 1,000 hours under 50 MPa of pressure at 50°C (122°F).

Good Dimensional Stability

 

The coefficient of linear thermal expansion (CLTE) of Ixef compounds is similar to that of many cast metals and alloys at ambient temperatures. Low mold shrinkage and the ability to maintain tight tolerances (as little as ± 0.05% length tolerances when properly molded) allow for high reproducibility.

COEFFICIENT OF LINEAR THERMAL EXPANSION OF IXEF RESIN
Ixef 10221.5 10-5K-1 (Flow direction)
Ixef 10223.6 10-5 K-1 (Transverse direction)
Steel1.2 10-5 K-1
Aluminum2.4 10-5 K-1
Brass1.8 10-5 K-1
Zinc3 10-5 K-1

Low and Slow Rate of Water Absorption

 

Ixef® PARA’s highly aromatic structure results in lower and slower water absorption than typical polyamides, which are highly sensitive to humidity. Water absorption for Ixef 1022 (50% glass fiber) is only 0.16% after 24 hours of water immersion at room temperature.

Good Chemical Resistance

 

Ixef® compounds are highly resistant to aqueous solutions of wide range of chemicals and cleaning fluids as well as to common solvents, such as:

  • Aliphatic hydrocarbons
  • Aromatic hydrocarbons
  • Chlorinated solvents
  • Ketones
  • Esters
  • Ethers
  • Glycols

Testing also shows good resistance to standard engine oil (Type SAE 10W30) after 2,000 hours at 120°C (248°F) and to automotive fuels after 2,000 hours at 40°C (104°F).