Epoxy Potting Crusher Backing Compound

$2.90 - $3.50
Min. Order
10 Liters
GET LATEST PRICE ON APP
Company Information

Yantai Darbond Technology Co., Ltd.

CN Manufacturer
Response Time
24h-48h
Response Rate:
88.9%
Transactions
---
10 Years Paid Supplier Gold Supplier Onsite Check
Learn More

Quick Details

Port: QINGDAO
Payment Terms: L/C,T/T
Supply Ability: 100 Ton/Tons per Year
Other Names: Crusher Backing Compound
Place of Origin: Shandong China
Classification: Double Components Adhesives
Main Raw Material: Epoxy
Usage: Construction,Transportation,mining industry
Brand Name: Darbond
Model Number: 3495
Color: Light grey
Shear Strenth(MPa): 15
Compressive Strength(MPa): 106
Hardness(Shore D): 80
Basic Material: Modified epoxy
Viscosity (Compoment A): 30000-60000MPa.s
Weight Ratio: 100:6.5
Skype: cutesnow212
Delivery Detail: 15 days
Packaging Detail: 10kg pail set

Darbond® Crusher Backing Compound

 

Features

  • Two component. b. Low volumetric shrinkage after cured, good filling effect.
  • Convenient for use, with long service life.
  • Much more safe compared to low melting point alloy.
  • Used for filling gap between wearable liner and cone for cone and gyratory crushers.
                

Introduction

Darbond® 3495 is a two-component, room temperature curing epoxy adhesive. Pour mixed material into cavities between wear-resistant liners and crusher body to achieve no gap filling and bonding; with excellent high loading impact resistance, cured material can strongly support the cone and liner, buffer, absorb energy and reduce vibration. It is convenient to use, with long service life and high cost performance.

 

Typical Application

  • Used for PY series cone crusher and cone/gyratory crusher (such as Nordberg, Sandvik) to fill the gap between liner and cone.
  • Also can be used to level for equipment installation. Mainly used for mine and smelting, hydraulic power plant, road building and building material etc. industries.
  • It also can be used for building, landscape stones, concrete and steel structure bonding and metal railing imbedding etc. 

 

Typical Properties of Mixed Materials

Typical Value    Range

Appearance      Light white grey thick liquid

Weight ratio            A:B=100:6.5

Volume ratio            A:B=8.55:1

Pot life(min)                   8-12

(10Kg@25°C)                              

Min. curing time before operation at room temperature (h)  

100% loading                8

 

Typical Performance of Cured Material

Specific Gravity (g/cm3) (GB/T13354-1992)      1.7

Hardness (Shore D) (GB/T2411-1980)              80

Shear Strength (MPa) (GB/T7124-1986)           15

Compressive Strength (MPa)(GB/T1041-1992)  106 

 

Typical Properties of Mixed Materials

Appearance      Light white grey thick liquid

Weight ratio            A:B=100:6.5

Volume ratio            A:B=8.55:1

Pot life(min)                8-12

(10Kg@25°C)                              

Min. curing time before operation at room temperature (h)  

100% loading                8

 

Typical Performance of Cured Materials

Specific Gravity (g/cm3) (GB/T13354-1992)      1.7

Hardness (Shore D) (GB/T2411-1980)              80

Shear Strength (MPa) (GB/T7124-1986)           15

Compressive Strength (MPa)(GB/T1041-1992)  106

 