|Payment Terms:||T/T,Western Union,Paypal|
|Supply Ability:||100000 Metric Ton/Metric Tons per Month|
|Other Names:||Silicone Sealant|
|Place of Origin:||Guangdong China|
|Main Raw Material:||Silicone|
|Model Number:||KL- 301G(ABC)|
|Adhesive property(After curing):||≥2.0(A1-A1,cohesive failure )|
|Shelf Life:||6 Months|
|Application:||Silicone gaskets sealant|
|Product name:||HTV silicone adhesive KL - 301G(ABC)|
|Certificate:||ISO SGS ROHS|
|Application ratio:||A:B:C=10:10:1(weight ratio)|
|Delivery time:||7-10 Working Days|
|Packaging Detail:||1KG/Bottle , 3KGS/Bottle, 10KGS/Bottle|
Three Component Silicone Adhesive
KL - 301G(ABC)
KL-301G(ABC) ,three component adhesive swiftly cured to be silicone rubber at hightemperature condition. Elastic and tight bond performance between cured type of silicone rubbers . The adhesive is characterized with good flowing ability before curing and elasticity electrical insulation property after cured.
Applied to silicone bonding with silicone like silicone rubber ring gaskets or seals which results in waterproof ,heat resistance ,insulation proof,moisture proof, shock absorbtion and sealing&bonding purpose.
Shelf Life: 6 Months
Mix viscosity(25℃),mΡa.s: 1000
Specific Gravity(g/cm³): 1.10
Operable time(25℃),h: 7.0
Curing time(170℃),min.: 1-2min
Tensile strength(Mpa): 7.0
Hardness(Shores A): 55±5
Adhesive property: ≥2.0(A1-A1,cohesive failure )
Volume resistance(Ω • cm): 1×1014
Dielectric strength(KV/mm): 20
l Application ratio: A:B:C=10:10:1(weight ratio)
l The adhesive is added by weight ratio and requires thorough mixture.
l Preheat the silicone rubber bonding areas a while before applying on the mixed adhesives KL-301G(ABC).
l Heating at temperature 180°C for 15-30 Seconds.
l Keep in tight seal packings
l Curing time of KL-301G(ABC) concerns with heat transfer efficiency and its packing sizes under the certain temperature.
l It also works for bonding cured type silicone rubber with a primer-treated metals (CL-24S-3 primer as base Coating)
l Testing compability of rubber and base material before using. Because the compound which contained sulfur, tin,arsenic,phosphorus,nitrogen,PB will cause bad curing during the curing process.