KL-301G(ABC), three component adhesive swiftly cured to be silicone rubber at high temperature condition.

Min. Order
2 Kilograms
Company Information

Shenzhen Kanglibang Science & Technology Co., Ltd.

CN Manufacturer
Response Time
Response Rate:
8 Years Paid Supplier Gold Supplier Onsite Check
Learn More

Quick Details

Port: Shenzhen
Payment Terms: T/T,Western Union,Paypal
Supply Ability: 100000 Metric Ton/Metric Tons per Month
Other Names: Silicone Sealant
Place of Origin: Guangdong China
Classification: Volatile Solvent Adhesives
Main Raw Material: Silicone
Usage: Other
Model Number: KL- 301G(ABC)
Type: Three Component
Appearance: Shallow yellow transparent liquid
Adhesive property(After curing): ≥2.0(A1-A1,cohesive failure )
Application: Silicone rubber
Shelf Life: 6 Months
Product name: HTV silicone adhesive KL - 301G(ABC)
Certificate: ISO SGS ROHS
Packing: 1KG/bottle
Keywords: Silicone Selant
Packaging Detail: 1KG/Bottle , 3KGS/Bottle, 10KGS/Bottle

Three Component Silicone Adhesive

KL - 301G(ABC)

KL-301G(ABC) ,three component adhesive swiftly cured to be silicone rubber at hightemperature condition. Elastic and tight bond performance between cured type of silicone rubbers . The adhesive is characterized with good flowing ability before curing and elasticity electrical insulation property after cured.



Applied to silicone bonding with silicone like silicone rubber ring gaskets or seals which results in  waterproof ,heat resistance ,insulation proof,moisture proof, shock absorbtion and sealing&bonding purpose.

Shelf Life: 6 Months



 Before curing

Mix viscosity(25℃),mΡa.s:             1000

Specific Gravity(g/cm³):                 1.10

Operable time(25),h:                  7.0

Curing time(170℃),min.:              1-2min


After curing

Tensile strength(Mpa):                  7.0

Hardness(Shores A):                   55±5

Elongation(%):                         450

Adhesive property:             ≥2.0(A1-A1,cohesive failure )

Volume resistance(Ω • cm):             1×1014

Dielectric strength(KV/mm):              20



 Application ratio: A:B:C=10:10:1(weight ratio)

The adhesive is added by weight ratio and requires thorough mixture.

Preheat the silicone rubber bonding areas a while before applying on the mixed adhesives KL-301G(ABC).

Heating at temperature 180°C for 15-30 Seconds.



 Keep in tight seal packings

Curing time of KL-301G(ABC) concerns with heat transfer efficiency and its packing sizes under the certain temperature.

It also works for bonding cured type silicone rubber with a primer-treated metals (CL-24S-3 primer as base Coating)

Testing compability of rubber and base material before using. Because the compound which contained sulfur, tin,arsenic,phosphorus,nitrogen,PB will cause bad curing during the curing process.