Rocky Silicone Structural Sealant for glazing

$1.00 - $10.00
GET LATEST PRICE ON APP
Company Information

Qingdao Rocky Industry Co., Ltd.

CN Manufacturer, Trading Company
Response Time
<24h
Response Rate:
70.6%
Transactions
US$ 600+
14 Years Paid Supplier Supplier Trade Assurance
Learn More

Quick Details

Port: qingdao
Payment Terms: L/C,T/T
Supply Ability: per your demand
CAS No.: Silicone Structural Glazing Sealant
Other Names: Silicone Structural Glazing Sealant
MF: Silicone Structural Glazing Sealant
EINECS No.: Silicone Structural Glazing Sealant
Place of Origin: China
Classification: Double Components Adhesives
Main Raw Material: Silicone
Usage: Construction
Brand Name: rocky
Model Number: sealant
color: black,white
Component A: 245kg
Component B: 19kg
Delivery Detail: within 30days after we recieved 30% deposit
Packaging Detail: Component A(base) 245kg (180L) Component B(curing agent) 19kg (18L

Silicone Structural Glazing Sealant from Qingdao Rocky Industry Co. Ltd tested by “China National Center for Test of Chemical Building Materials” according to the National Standard GB16776-2005.

Report No: Betc-hj-2009-154(A)                         Report Date:2010/01/06

Products Name:  Silicone Structural Glazing Sealant

Sample Produce date:  0910021

Standard: The National Standard GB16776-2005

Test term: Room temperature,23°C±2°C, Humidity, 50±5%

No

Item

The standard

Test result

Individual evaluate

1

Appearance

Fine, Homogeneous paste, there should be no bubbles, no crust,no gel,no liquid things which isn’t quickly evenly spread.

In line with the standards

Passable

2

Flow degree, mm

Vertical, mm

≤3

0

Passable

Level

No deformation

No deformation

Passable

3

Working time

Mix time, min

≥20

20

Passable

Extrusion ability, S

≤10

2.9

4

Tack Free Time, h

≤3

0.9

Passable

5

Hardness, Shore (A)

20-60

38

Passable

6

Heat ageing

Hot weight loss,%

≤10

2.5

Passable

Crack

No

No

Passable

Chalking

No

No

Passable

7

Adhesion

 

elongation

23°C

Tensile strength, Mpa

≥0.60

1.09

Passable

Adhesion break area,%

≤5

0

Elongation when Maximum Tensile modulus, Mpa

≥100

187.1

90°C

Tensile strength, Mpa

≥0.45

0.79

Passable

Adhesion break area,%

≤5

0

-30°C

Tensile strength, Mpa

≥0.45

1.73

Passable

Adhesion break area,%

≤5

0

After in water

Tensile strength, Mpa

≥0.45

1.05

Passable

Adhesion break area,%

≤5

0

After UV -water immersion

Tensile strength, Mpa

≥0.45

0.96

Passable

Adhesion break area,%

≤5

0

8

Tensile modulus

23°C

at 10% elongation/kpa

-

87.2

/

at 20% elongation/kpa

-

244.3

/

at 40% elongation/kpa

-

430.3

/

Note: 1-Test base material:8mm float glass and 4mm Anodized aluminum plate,

2-Cleaning solvent: 50% Acetone 

Conclusion: The sample was tested in line with the standards for GB16776-2005.